Goobay professional lead-free solder, composition: 3.5 % silver, 0.7 % copper, 95.8 % tin, flux content: 2.5 %, melting point 217 °C, ø 1.0 mm, 100 g.
You are CHF50.00 short of free shipping!
Goobay professional lead-free solder, ø 1.0 mm, 100 g
The Goobay professional solder is a lead-free solder wire with a diameter of 1.0 mm and a weight of 100 g. It is ideal for soldering work on electrical components and devices such as circuit boards, PCBs, SMDs, DIP, cables, televisions, headphones or microphones. The composition consists of 3.5 % silver (Ag), 0.7 % copper (Cu) and 95.8 % tin (Sn), which results in improved electrical conductivity and optimum flow properties. The integrated flux content of 2.0 % enables convenient and effective soldering without having to rework the solder joints. The melting point is 217 °C.
Details
- Flux-filled solder wire with a thin diameter of 1 mm for particularly easy dispensing and soldering of delicate components
- High proportions of silver and copper (Sn3.5Ag0.7Cu) ensure optimised flow behaviour and improved surface quality for lead-free soldering
- Simple, homogeneous wetting of the solder joint thanks to the rosin flux core
- No-clean solution with continuous flux cores, eliminating the need to clean the solder joint after use
- Reduced splashing behaviour for increased user safety and protection of the workpiece
- Halogen-free and low smoke emission
- Perfect for soft soldering at low temperatures in machine and hand soldering applications
Note on spare parts: technikdepot.ch does not want to sell counterfeit products - therefore all our spare parts are explicitly not original brand spare parts, but produced by independent third-party manufacturers. Of course, all the usual quality requirements are met, but they do not have any brand logos printed on them.
192
Data sheet
- Country of origin
- CN
Reviews (0)
Based on 0 reviews
-
Goobay professional lead-free solder, composition: 3.5 % silver, 0.7 % copper, 95.8 % tin, flux content: 2.5 %, melting point 217 °C, ø 1.0 mm, 100 g.